SQB无石棉橡胶复合板
这种产品是由高强度芳纶纤维、植物纤维同丁腈橡胶、无机矿物质在高温、高压下压延而成，是石棉橡胶板的替代产品。 |
 |
NON ASBESTOS JOINT SHEET SQB
This products is made from“Kevlar”Aramid fiber,Veg-etable fiber,Mineral fiber
compressed and calendered under high temperature and pressure into a sheet form. It elimi-nates asbestos-rubber sheet essentially and thoroughly. |
| 规格：SIZE |
|
|
厚度(mm)
Thickness
|
密度(g/cm3)
Density
|
1000
4000
2000
|
≤1500 |
0.5,1.0,1.5,2.0,3.0,4.0,5.0 |
1.8~2.0 |
|
主要性能 MAIN PROPERTIES |
| 颜色Color |
黑Black |
红red |
绿白
green-white |
| 温度Temperature(
℃
) |
400 |
300 |
300 |
| 压力Pressure(kgf/cm2) |
100 |
70 |
70 |
| 压缩率Compressibility(%)ASTM F36 |
7-17 |
7-17 |
7-17 |
| 回弹率Recovery(%)ASTM F36 |
≥45 |
≥45 |
≥45 |
| 横向抗拉强度Horizontal Tensile Strenght (N/mm2) ASTM F152 |
10 |
12 |
15 |
耐油性Oil Resistance
(zai150
℃
3号标准油中浸泡5小时 ASTM No.3oil-5h 150
℃
增厚率Thicknness lncrease(%)
增重率Weight Lncrease(%)
抗拉强度变化率Variation of Tensile Strenght (N/mm2) ASTM F152 |
0~5
≤10
-30
|
0~5
≤10
-30
|
0~5
≤10
-25
|
| 泄漏率Leakage rate (ml/min)DIN 3535/4 |
0.5 |
0.5 |
0.5 |
烧矢量lgnition loss(%) JB/T6628
(300
℃灼烧3小时 Under 300
℃
Temp igniting for 3 houres)
|
≤8 |
≤8 |
≤10 |
| 应力松弛Stress Relaxation (N/mm2)DIN 53913 |
≤25 |
≤25 |
≤25 |
|
 上述产品均可內衬金属丝网：镀锌铁丝网，铜丝网，AISI304钢丝网等
所规定的最高使用温度和最大使用压力不能同时发生，且不能适合所有厚度的垫片 |
| 垫片所能使用的温度和厚度有关，垫片越薄，相应的温度和压力特性越好。 |